Jurong Ruixin Environmental Protection Materials Co., Ltd. invites you to the 2025 SMM Zinc Industry Conference

Against the backdrop of the in-depth advancement of the "dual carbon" strategic goals, the zinc industry, as a vital pillar in the basic materials sector, is undergoing a profound transformation from traditional manufacturing to green recycling. The global trade landscape is undergoing rapid reconfiguration, and the zinc industry chain is facing multiple challenges: the low-carbon entry thresholds in the international market continue to rise, regional supply chain barriers are becoming increasingly prominent, and technical trade measures are forming differentiated encirclements on niche sectors such as galvanizing, zinc oxide, and zinc salts. Meanwhile, breakthroughs in the recycling technology of secondary zinc resources and the construction of a circular economy system are becoming strategic pivots for reshaping the global zinc industry's competitive landscape.

Currently, China's zinc industry urgently needs to drive the transformation and upgrading of the entire industry chain through technological innovation. With the joint support of upstream and downstream enterprises, industry associations, and relevant parties in the zinc industry, the 2025 SMM Zinc Industry Conference & the 7th Hot-Dip Galvanizing Industry Development and Technological Innovation Forum, and the 13th Zinc Salt, Zinc Oxide, and Secondary Zinc Resources Development Forum are set to be held from August 14-16. The conference will closely revolve around the high-quality development needs of the zinc industry, with the theme of "Zinc Momentum, Intelligent Recycling, New Development". It will focus on hot topics such as industrial market development, policy planning, technological innovation, equipment upgrades, new materials and applications, and supply and demand transactions. We sincerely invite global zinc smelting, processing, application, and recycling enterprises to jointly discuss collaborative development mechanisms, address trade changes through technological breakthroughs, and work together to draw up a blueprint for the high-quality and sustainable development of the zinc industry!

Jurong Ruixin Environmental Protection Materials Co., Ltd. hereby extends a warm invitation to gather at this industry summit event. Let us join hands, draw up a development blueprint together, and jointly propel the zinc industry towards a more prosperous, green, and sustainable future.

Click on the registration form now to easily complete your conference registration and jointly witness and participate in this extraordinary and far-reaching industry event, creating a brilliant new chapter together!

Jurong Ruixin • Pioneer of New Hot-Dip Galvanizing Processes

Jurong Ruixin Environmental Protection Materials Co., Ltd. was established in September 2015. The company is located at the foot of Maoshan Mountain, a Taoist holy site, adjacent to Nanjing in the west and Suzhou, Wuxi, and Changzhou in the east, at the core of the Yangtze River Delta economic circle. Our products are widely applied in surface treatment technology services for industrial cleaning and coating, electrophoresis, and hot-dip galvanizing processes. Since 2018, our technical personnel have developed a series of new processes for the hot-dip galvanizing industry, targeting the current status of hot-dip galvanizing processes, to reduce production costs for hot-dip galvanizing enterprises, make hot-dip galvanizing processing more environmentally friendly, and have gained widespread application and market recognition.

The following products are launched to meet the diverse process needs of customers:

Ammonium-free flux aid, Zinc fume inhibitor, Zinc ash reduction and leakage prevention agent, High-aluminum leakage-proof plating agent, Flux-aiding ammonium agent, Zinc ash reduction and explosion-proof agent, Mist suppression and degreasing agent, Pickling inhibitor

Dedicated to solving issues of plating leakage, zinc consumption reduction, and zinc ash reduction in hot-dip galvanizing

Our company adheres to the principles of customer first, environmental protection first, quality first, and service first!We look forward to collaborating with you to create a brilliant future together!

I. Product Introduction

1. This product is a composite of polymer nano-modified materials and proprietary solvents, an environmentally friendly material that contains no cadmium, lead, mercury, fluorine, bismuth, or hexavalent chromium. After using this product, hot-dip galvanizing can achieve "0" ammonium chloride operation for the fluxing agent and "0" ammonia water for iron removal, truly realizing an ammonium-free fluxing process. On this basis, it will significantly reduce zinc fumes generated during the galvanizing process, improve zinc utilization, reduce the environmental protection pressure on galvanizing enterprises, and lower galvanizing costs.

2. This product also possesses excellent anti-explosion properties. After using this product, there is no need to add anti-explosion agents or other similar products to the fluxing agent, thereby reducing usage costs.

II. Usage Instructions

1. When using this product, add the smokeless fluxing agent to the fluxing tank at a 2% dosing ratio. The ammonium chloride content in the fluxing agent should be reduced to 0 g/l, with zinc chloride at 120-150 g/l, and the pH should not exceed 3.5. After adding and thoroughly mixing, it can be used. The temperature of the fluxing agent should generally not be lower than 55°C.

2. After using this product, the original ammonia water/hydrogen peroxide iron removal process in the fluxing tank will no longer be used. Instead, a special iron removal agent (compatible with our company's smokeless fluxing agent) should be added during the iron removal process (online iron removal equipment already installed in galvanizing plants can still be used) to ensure "0" ammonium introduction during the iron removal process and "0" ammonium operation of the smokeless fluxing process.

3. This product is a consumable, and its consumption rate is directly related to production. Generally, for every 200-250 mt of galvanized parts produced, 25-30 kg of this product needs to be replenished.

4. During the production process, when water needs to be replenished to the process tank due to water level drop, this product should be added to the process tank at a 1% ratio of the replenished water volume to ensure concentration balance.

5. Comparison of fluxing process parameters before and after using this product

6. For the use of the accompanying special iron removal agent, production lines with online iron removal equipment already installed can be configured with liquid packaging (1 mt drums) to perfectly adapt to the existing online iron removal equipment. Production lines without online iron removal equipment can be configured with solid packaging (25 kg/bag), and centralized tank dumping for iron removal can be carried out based on the actual iron content of the fluxing agent to achieve fluxing agent cleaning, reduce zinc slag production, and thus lower production costs.

III. Packaging and Storage

1. This product is packaged in 25L plastic drums or mt drums and stored in a dry and cool place.